Item Details

Product Description

Heat Resistant Waterborne Liquid Epoxy Resin Anti Rust Coating Appliance Paint WQ-WL175

Features:

? Acrylic modified;aging resistance>300h;

? Excellent shear stability,able to be grinded with dispersions directly;

? Fast surface dry,quick hardness increase,and excellent anti-rust property;

? Drying way:air dry oxidative cross-linking type;water based drier is needed for making paint;

? Product form:solid content:75%;

? High solid content,low viscosity,good anti-sagging property,single spraying film thickness of above 50 micron

? Suitable for air-drying or low temperature baking type metal anti-rust paint


Technical Index

Composition:Water based epoxy resin,cosolvent,neutralizing agent

Viscosity(mPa.s):150±50(at diluting ratio of 1:1,rotational viscometer)

Non-volatile Matters(%)75±1

Appearance:brown viscous liquid


Properties:

Excellent anti-corrosivity,designed for the preparation of anti-rust base coating;it can be made into air drying and low temperature baking type antirust paint;the paint film has excellent drying property and anti-corrosivity.

The product can be stored stably under weak alkaline condition,but settles down under the acidic conditions,especially when acidic pigment is added.Thus,the stable emulsion and lacquering shall be stored under weak alkaline condition.PH value can always be adjusted by triethylamine or ammonia water,and the emulsion viscosity will increase as the PH value increases.

WQ-WL175 can be diluted with deionized water.When it is diluted,acidic or impure water will instabilize the system.After its pH is adjusted,the emulsion has good storage stability,can be diluted with lower alcohol or alcohol ether,or clean water after passing the test.


Instructions:

WQ-WL175 can be diluted with water to milky white emulsion,which can be dried by oxidative cross-linking by adding solvent or water based drier at normal temperature or baking at low temperature.Before use,the solvent based drier need to be diluted by the solvent,such as butyl alcohol or ethanol.The consumption of associated drier of this company is about 8%of the resin consumption.The paint film dries very fast.The surface drying time is about 20 min,and the hard drying time is about 4 h.After 24 h,the paint film has good strength.This product has excellent shear stability,and can be grinded with dispersions directly.


Storage:

The product should be stored in cool,dry,ventilated place.The quality guarantee period is 6 months,and the expired products can still be used after passing the inspection.


Basic properties:

No.

Item

Index

Standard

1

Appearance

Smooth,glossy

GB/T9761-88

2

Color

Grey,matt


3

Surface drying time(h)

=0.5

GB/T1728-79/89

4

Hard drying time(h)

=4

GB/T1728-79/89

5

Adhesion(Cross-cut tape test),grade

=1

GB/T1720-79

6

Impact

=50

GB/T1732-1993

7

Hardness(double pendulum)

=0.6

GBT1730-93

8

Flexibility(mm)

1

GB/T1731-1993

9

gasoline resistance(120#)

=24h

GB/T1734-93

10

Acid resistance(0.05mol/l H2SO4)

=24h


11

Alkaline resistance(0.1mol/l,NaOH)

=4h


12

Water resistance(at 25?,h)

=240

GB/T1733-193

13

Resistance to heat and humidity(at 48?,96%,h)

>240(50-60u)

GB/T1740-79

14

Salt fog resistance(white board,h)

=240(50-60u)

GB/T1771-1991

15

Salt fog resistance(white board,h)

=1000(80-100)

GB/T1771-1991

??14.png

Other Product:


product name

non-
 volatile

PH

viscosity
 (mPa.s)

specific
 gravity

properties

application

WQ-WL175

76±2

/

100-200*

1.02±0.01

excellent salt fog-spray resistance,in the early dry  good resistance to water

air-drying or low temperature baking antirust coatings

WQ-EE640

40±2

8-10

100-500

1.02±0.01

low odor,excellent salt fog-spray resistance,in the  early dry good resistance to water,easy operation

air-drying or low temperature baking antirust coatings

WQ-EA670

72±2

/

120-220*

1.02±0.01

dry quickly,high hardness,good weather resistance

air-drying or low temperature baking antirust coatings  and top coatings

WQ-EA632

32±2

8-10

1000-2000

1.02±0.01

low odor,dry quickly,high hardness,high gloss,good  weather resistance

air-drying or low temperature baking antirust coatings  and top coatings

WQ-AK360

62±2

/

30-120

1.00±0.01

dry quickly,high hardness,suitable for high temperature  and high humidity environment

air-drying or low temperature baking primer and one  coat paint